GPA6 UD tape is a mixture of 6 continuous glass fibers and polyamide 6. It is a lightweight structural material.
GPA6 UD Tapes Features
- 60% glass fiber content.
- Tensile strength reaches 830MPa.
- PA (Polyamide) 6 resin with high thermal stability.
- 0°/90° cross laying can be adopted to obtain stronger mechanical strength.
Advantages of GPA6 UD Tapes
- Low cost.
- Lightweight.
- High tensile and flexural strength.
- Impact-resistant.
- No VOC, completely recyclable.
Parameters
- 0°Unidirectional Laminate Mechanical Properties
| TEST ITEMS | TEST STANDARDS | CONDITION | UNITS | TYPICAL VALUE |
|---|---|---|---|---|
| Density | ISO1183 | 23℃ | g/cm3 | 1.72 |
| Fiberglass Content | ISO3451 | 23℃ | %wt | 60 |
| Tape Thickness | / | 23℃ | mm | 0.30 |
| Tensile Strength | ISO527-3/Tape | Dry,10mm/min | MPa | 830 |
| Flexural Strength | ISO14125 | Dry,5mm/min | MPa | 1050 |
| Flexural Modulus | ISO14125 | Dry,5mm/min | GPa | 40 |
| Inter-laminar Shear Strength | ISO14130 | 1mm/min | MPa | 45 |
| Compressive Strength | ISO14126 | 1mm/min | MPa | 340 |
- 0/90 Organo Sheet Mechanical Properties
| TEST ITEMS | TEST STANDARDS | CONDITION | UNITS | TYPICAL VALUE |
| Flexural Strength | ISO14125 | Dry,5mm/min | MPa | 560 |
| Flexural Modulus | ISO14125 | Dry,5mm/min | GPa | 26 |
- Note1: Product performance may be different from the above values.
- Note2: Typical values are the average laboratory data, only for reference.
- Note3: According to different equipment, molds, and customer requirements, the process must be appropriately adjusted.
Application of GPA6 UD Tapes
- Infrastructure: Used in civil engineering applications to reinforce concrete structures.
- Aerospace: Used to reinforce structural components of aircraft, vehicles, helping to reduce weight and improve performance.
- Automotive: Used to manufacture lightweight components of vehicles such as chassis components and body panels.
- Marine: Used in ship construction to reinforce the hull and other structural elements.
- Sports and Recreation: Commonly used in the production of sporting goods such as bicycles, tennis rackets and skis.
- Wind Energy: Used in wind turbine blades to reinforce composite materials.
Customized Service
TOPOLO is dedicated to the research and design of new composite materials for lightweight solutions. Our products of continuous fiber-reinforced thermoplastic composites are ideal choices for your economical and high-quality requirements.