Continuous fiber-reinforced thermoplastic laminates that can be stamped or thermoformed into various shapes. The shaped part can be over-molded with additional resin for added stiffness and part integration. Moreover, its significant strength and stiffness properties are, in many cases, superior to most metals. TOPOLO series multilayer cross-ply laminates offer a viable replacement to metal parts in the honeycomb panel applications.

Features

  • Significant weight reduction;
  • Superior strength and stiffness to steels;
  • Excellent performance in crash applications;
  • Less creep than short­ fiber-reinforced resins;
  • High thermal aging properties;
  • Flame-retardant.

Our products range from 2 layers to 9 layers and differ by lamination methods, thickness, flexural strength, and modulus. Variations are available with glass fiber, carbon fiber, and both.

2 Layers FRP Sheets

Lamination0/90/0/90/090/0/90/0/90
Thickness1.2mm0.6mm
Flexural Strength630MPa350MPa
Flexural Modulus25GPa7.5GPa

5 Layers FRP Sheets

Lamination0/90/0/90/090/0/90/0/90
Thickness1.2mm1.2mm
Flexural Strength630MPa350MPa
Flexural Modulus25GPa7.5GPa

7 Layers FRP Sheets

Lamination0/90/0/90/0/90/090/0/90/0/90/0/90
Thickness1.6mm1.6mm
Flexural Strength530MPa370MPa
Flexural Modulus19GPa9GPa

9 Layers FRP Sheets

Lamination0/90/…/90/090/0/…/0/90
Thickness2.15mm2.15mm
Flexural Strength450MPa350MPa
Flexural Modulus18GPa8.5GPa

Compound Fabric Of FRP And PP

Lamination0/90/Fabric/0/90/090/0/Fabric/90/0/90
Thickness2.5mm2.5mm
Flexural Strength300MPa230MPa
Flexural Modulus14GPa7.6GPa

PP Compound Fabric

Lamination3*1500g/m2
Thickness3mm
Flexural Strength190MPa
Flexural Modulus9GPa

Get a Quote